Adequately stabilized and exposed Cu/CuₓO heterojunction on porous carbon nanofibers by StuffsEarth

Inexpensive and readily available copper-based catalysts are considered ideal for the electrochemical CO₂ reduction reaction (CO₂RR) to produce multi-carbon products. The presence of copper oxides is crucial for generating high-value-added products in CO₂RR.

However, the inevitable side hydrogen evolution reaction and the easy self-reduction reaction of copper oxide under the negative potentials diminish the catalytic activity and selectivity of CO₂RR. Currently, designing a stable phase with both resistance to electrochemical self-reduction and high CO₂RR activity is challenging.

Recently, a research team led by Prof. Chuanxin He from Shenzhen University, China, sought to fully utilize the confinement effect and carrier effect of porous carbon nanofiber substrates on metal nanoparticles, significantly enhancing the exposure of active sites Cu/Cu_xO heterojunctions at the catalytic reaction interface.

The catalyst could maintain the structural stability of copper oxides under a current density of 400 mA cm^‒2 and achieve an excellent CO₂RR performance to ethanol with a Faradaic efficiency as high as 70.7% and a mass activity of 8.4 A mg^‒1.

In this research, highly-dispersed copper nanoparticles within carbon nanofiber were firstly prepared via electrospinning, then the O₂-plasma treatment was introduced to simultaneously create Cu/Cu_xO heterostructure and opening mesopores throughout those carbon nanofibers.

Specifically, the opening mesopores throughout carbon nanofibers can fully expose the Cu/Cu_xO sites to the three-phase interface compared with untreated carbon nanofibers, leading to high and stable catalytic activity with low metal loading amount.

Combined with the physical characterizations and in-situ spectral characterizations such as infrared and Raman spectroscopy analysis, a dynamic stabilized state of Cu_xO and the key signals of *CO and C–C bond are observed during the CO₂RR process. Additionally, DFT calculations show that the presence of Cu_xO promotes the spillover of *CO intermediate to the Cu/Cu_xO interface, which can decrease the C–C coupling energy barrier to form C₂H₅OH during the CO₂RR process.

The carbon substrate can enhance electron transport and act as an electron donor to neutralize the reduction of Cu_xO under a negative potential, which assists the stability of Cu/Cu_xO heterostructure and maintains 213-h stability at high current densities. The results were published in Chinese Journal of Catalysis.